2024 Seamless Aluminum Tubing Pipe 2.6M High Strength Corrosion Resistance

Name: 2024 Seamless Aluminum Tubing Pipe 26M High Strength Corrosion Resistance
Brand: HUANYU
Price: 1 USD

China 2024 Seamless Aluminum Tubing Pipe 2.6M High Strength Corrosion Resistance wholesale

Brand Name : HUANYU

Model Number : HYT2024T

Place of Origin : CHINA

MOQ : 2 METRIC TONS

Price : Negotiable

Payment Terms : T/T

Supply Ability : 45 Metric Tons Per Month

Delivery Time : 21 days

Packaging Details : Plywood Case

Product Name : 2024 Seamless Aluminum Tubing

Ultimate Tensile Strength : 186MPa

Tensile Yield Strength : 75.8 MPa

Hardness, Brinell : 47

Elongation at Break (Typical; 1/2 in. (12.7 mm) Diameter) : 21 %

Melting Point : 502 - 638 Degrees C

Annealing Temperature : 413 Degrees C

Solution Temperature : 256 Degrees C

Length : 2.6M

Diameter : 58.0MM

Wall Thickness : 6.0MM

Contact Now

2.6M High Strength Corrosion Resistance 2024 Seamless Aluminum Tubing

2024 is a typical hard aluminum alloy in the aluminum-copper-magnesium series. Its composition is reasonable and the overall performance is better. Many countries produce this alloy, which is used in duralumin. The characteristics of the alloy are: high strength, a certain degree of heat resistance, and can be used as working parts below 150°C. At temperatures higher than 125°C, the strength of 2024 alloy is higher than that of 7075 alloy. The forming properties in the hot state, annealing and new quenching state are better, and the heat treatment strengthening effect is significant, but the heat treatment process is strict. The corrosion resistance is poor, but it can be protected by covering it with pure aluminum; it is easy to produce cracks, but it can also be riveted by special technology. It is widely used in aircraft structures, rivets, truck wheels, propeller components and various other structural parts.

Physical Properties

	Metric	English	Comments

Density	2.78 g/cc	0.1 lb/in³	AA; Typical
Mechanical Properties

Hardness, Brinell	47	47	AA; Typical; 500 g load; 10 mm ball
Ultimate Tensile Strength	186 MPa	27000 psi	AA; Typical
Tensile Yield Strength	75.8 MPa	11000 psi	AA; Typical
Elongation at Break	20 %	20 %	AA; Typical; 1/16 in. (1.6 mm) Thickness
Elongation at Break	22 %	22 %	AA; Typical; 1/2 in. (12.7 mm) Diameter
Modulus of Elasticity	73.1 GPa	10600 ksi	AA; Typical; Average of tension and compression. Compression modulus is about 2% greater than tensile modulus.
Ultimate Bearing Strength	345 MPa	50000 psi	Edge distance/pin diameter = 2.0
Bearing Yield Strength	131 MPa	19000 psi	Edge distance/pin diameter = 2.0
Poisson's Ratio	0.33	0.33
Fatigue Strength	89.6 MPa	13000 psi	AA; 500,000,000 cycles completely reversed stress; RR Moore machine/specimen
Machinability	30 %	30 %	0-100 Scale of Aluminum Alloys
Shear Modulus	28 GPa	4060 ksi
Shear Strength	124 MPa	18000 psi	AA; Typical
Electrical Properties

Electrical Resistivity	3.49e-006 ohm-cm	3.49e-006 ohm-cm	AA; Typical at 68 Degrees F
Thermal Properties

CTE, linear 68 Degrees F	23.2 µm/m- Degrees C	12.9 µin/in- Degrees F	AA; Typical; Average over 68-212 Degrees F range.
CTE, linear 250 Degrees C	24.7 µm/m- Degrees C	13.7 µin/in- Degrees F	Average over the range 20-300 Degrees C
Heat Capacity	0.875 J/g- Degrees C	0.209 BTU/lb- Degrees F
Thermal Conductivity	193 W/m-K	1340 BTU-in/hr-ft²- Degrees F	AA; Typical at 77 Degrees F
Melting Point	502 - 638 Degrees C	935 - 1180 Degrees F	AA; Typical range based on typical composition for wrought products 1/4 inch thickness or greater. Eutectic melting is not eliminated by homogenization.
Solidus	502 Degrees C	935 Degrees F	AA; Typical
Liquidus	638 Degrees C	1180 Degrees F	AA; Typical
Processing Properties

Annealing Temperature	413 Degrees C	775 Degrees F
Solution Temperature	256 Degrees C	493 Degrees F

2024 Seamless Aluminum Tubing Pipe 2.6M High Strength Corrosion Resistance

Product Tags:

2024 Seamless Aluminum Tubing Pipe 2.6M High Strength Corrosion Resistance Images

Inquiry Cart 0

Send your message to this supplier


*From:	Your email address is incorrect!
*To:	Chongqing Huanyu Aluminum Material Co., Ltd.
*Subject:	Subject is empty!
*Message:	For the best results, we recommend including the following details: -Self introduction -Required specifications -Inquire about price/MOQ Characters Remaining: (0/3000) Please enter 20 to 3000 characters to contact this supplier!

2024 Seamless Aluminum Tubing Pipe 2.6M High Strength Corrosion Resistance

2024 Seamless Aluminum Tubing Pipe 2.6M High Strength Corrosion Resistance

2024 Seamless Aluminum pipe

Corrosion Resistance Seamless Aluminum Tubing

Seamless High Strength Aluminum pipe

2024 Seamless Aluminum Tubing Pipe 2.6M High Strength Corrosion Resistance Images